The steps of quality extruded aluminum t slot during extrusion
Release time:
2022-06-14 15:27
Source:
The quality extruded aluminum t slot is a processing method that puts aluminum alloy into the extrusion cylinder and applies a certain pressure to make it flow out from a specific die hole, so as to obtain the required cross-sectional shape and size. The processing method has low cost, high efficiency and simple operation, and occupies a considerable proportion in the modern industrial production system. What are the steps in the extrusion of quality extruded aluminum t slot? Let's take a look together!
1. Lay the prepared aluminum rods on the rack. A certain gap should be reserved between the aluminum rods. Be careful not to stack the aluminum rods, otherwise it will increase the difficulty of the extruder, and it is easy to cause aluminum alloys during operation. The rod falls and hurts the staff;
2. Operate in strict accordance with the process flow, place 12 aluminum rods in the furnace, and heat them at room temperature. When the heating time reaches 3.5 hours, the temperature reaches 480 °C, and then normal production can be carried out after 1 hour of heat preservation;
3. At the same time, put the extrusion die into the furnace for heating, so that the die temperature also reaches 480℃;
4. After the heating and heat preservation of the aluminum rod and the mold are done, put the mold into the die seat of the extruder and prepare it;
5. Put the cut aluminum rod into the raw material inlet of the extruder to prepare for extrusion;
6. Entering the extrusion stage. After the extruded profile comes out of the discharge hole, it is pulled by the tractor, and then the length and size are determined for cutting, and then the aluminum profile is sent to the leveling table for straightening. The aluminum profiles can then be transported to the finished product area for cutting to length.
7. Load the cut quality extruded aluminum t slot into the material frame according to the requirements, transport it to the aging zone, enter the aging furnace and carry out aging treatment, when the aging temperature reaches 200 ℃, keep the heat for 2 hours, and then wait for the furnace to be released;
quality,extruded,aluminum,t,slot
Next Page
Next Page
Sweep the phone website
Contact Us
Tel: 86-512-53640771
Fax: 86-512-53640769
E-mail：sales@alumag.com.cn(Domestic sales)
export@alumag.com.cn(Export)
Web:http://www.alumag.com.cn/
Address: No. 9, Xingang East Road, Liujiagang, Fuqiao Town, Taicang City, Jiangsu Province, China